Investigation of luminescent properties inherent to SrTiO₃:Pr³⁺ luminophor with Al impurity
The red-emitting SrTiO₃:Pr³⁺,Al luminophors that can be used for the white light emitting diodes (LEDs) were prepared using the sol-gel method. The starting materials were SrCl₂, Ti (O – i – C₃H₇)₄, Al(NO₃)₃·9H₂O and PrCl₃. The reaction between them results in a mixture of compounds that transfor...
Збережено в:
| Дата: | 2011 |
|---|---|
| Автори: | , , , , , |
| Формат: | Стаття |
| Мова: | English |
| Опубліковано: |
Інститут фізики напівпровідників імені В.Є. Лашкарьова НАН України
2011
|
| Назва видання: | Semiconductor Physics Quantum Electronics & Optoelectronics |
| Онлайн доступ: | http://dspace.nbuv.gov.ua/handle/123456789/117792 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Цитувати: | Investigation of luminescent properties inherent to SrTiO₃:Pr³⁺ luminophor with Al impurity / O.M. Marchylo, L.V. Zavyalova, Y. Nakanishi, H. Kominami, A.E. Belyaev, G.S. Svechnikov // Semiconductor Physics Quantum Electronics & Optoelectronics. — 2011. — Т. 14, № 4. — С. 461-464. — Бібліогр.:11 назв. — англ. |
Репозитарії
Digital Library of Periodicals of National Academy of Sciences of Ukraine| Резюме: | The red-emitting SrTiO₃:Pr³⁺,Al luminophors that can be used for the white
light emitting diodes (LEDs) were prepared using the sol-gel method. The starting
materials were SrCl₂, Ti (O – i – C₃H₇)₄, Al(NO₃)₃·9H₂O and PrCl₃. The reaction
between them results in a mixture of compounds that transform into single-phase
SrTiO₃:Pr³⁺,Al after annealing in air. Displacement of Ti out of the SrTiO₃ lattice caused
by substitution with Al and formation of individual crystalline TiO₂ phase (rutile) were
observed. PL spectra show the high-intense red peak (λ = 617 nm), the same high-intense
peak with the full width at half maximum (FWHM) 20 nm was found in
cathodoluminescence spectra. The increase of the aluminium concentration from 0 up to
15 mol.% leads to approximately two-fold increase in the luminance. The latter increases
from 180 up to 350 cd/m²
at the anode voltage 10 kV and current density 30 μA/cm²
. |
|---|