Influence of oxygenation time on crack growth in titanium alloy under cyclic bending
The paper contains the results of tests on the fatigue crack growth in Ti–6Al–4V titanium alloy. Plane specimens of 4 mm in thickness with a unilateral notch were used. An analysis of crack growth was carried out for specimens without and after 2 and 4 h oxygenation process as well as fatigue crack...
Gespeichert in:
| Datum: | 2011 |
|---|---|
| Hauptverfasser: | , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2011
|
| Schriftenreihe: | Фізико-хімічна механіка матеріалів |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/138129 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Influence of oxygenation time on crack growth in titanium alloy under cyclic bending / D. Rozumek, M. Hepner // Фізико-хімічна механіка матеріалів. — 2011. — Т. 47, № 1. — С. 82-86. — Бібліогр.: 8 назв. — англ. |