The influence of current density of deposition on Zn–Ni coatings properties
Zn–Ni coatings were deposited under galvanostatic conditions at current density in the range of 20 to 60 mA⋅cm⁻². The influence of current density of deposition on the surface morphology, chemical and phase composition and corrosion resistance was investigated. Structural investigations were perform...
Gespeichert in:
| Datum: | 2011 |
|---|---|
| Hauptverfasser: | , , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2011
|
| Schriftenreihe: | Фізико-хімічна механіка матеріалів |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/138346 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | The influence of current density of deposition on Zn–Ni coatings properties / K. Wykpis, M. Popczyk, J. Niedbała, A. Budniok, E. Łągiewka // Фізико-хімічна механіка матеріалів. — 2011. — Т. 47, № 6. — С.107-114. — Бібліогр.: 12 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of UkraineSchreiben Sie den ersten Kommentar!