New method for measuring magnetoelectric effect in pulsed magnetic fields
A new measurement method for magnetoelectric effect in pulsed magnetic fields has been developed. The pulsed field system generates in a bore of 25 mm fields up to 10.0 T with a typical pulse duration of 20 ms. Besides the magnetization, the system allows the measurement of the magnetoelectric effec...
Gespeichert in:
Datum: | 2006 |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | English |
Veröffentlicht: |
НТК «Інститут монокристалів» НАН України
2006
|
Schriftenreihe: | Functional Materials |
Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/144370 |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
Zitieren: | New method for measuring magnetoelectric effect in pulsed magnetic fields / E.D. Bueno-Baques, J. Matutes-Aquino, V. Corral-Flores, M. Botello-Zubiate, D. Rios-Jara, R. Grossinger // Functional Materials. — 2006. — Т. 13, № 2. — С. 283-287. — Бібліогр.: 9 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of UkraineZusammenfassung: | A new measurement method for magnetoelectric effect in pulsed magnetic fields has been developed. The pulsed field system generates in a bore of 25 mm fields up to 10.0 T with a typical pulse duration of 20 ms. Besides the magnetization, the system allows the measurement of the magnetoelectric effect in both transversal and longitudinal modes. The magnetoelectric effect on well known cobalt ferrite/ barium titanate composites and single-phase materials was measured as a function of the temperature. A maximum magnetoelectric coefficient of 1.5 mV/(cm•Oe) was obtained for a composite with a composition of 50 mass % ferrite sintered at 1200 °C. A model to explain the results obtained by this measurement method is discussed. |
---|