Features of formation of crystallographic texture and properties in Ti-3Al-2.5V titanium alloy during tubes manufacture

Texture formation processes at all technological stages of tube manufacture were considered. It has been established that at the stage of hot deformation and manufacture of TREX tubes, tangential and radial textures are formed, a large share of tangential component of the texture. Influence of main...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Datum:2019
Hauptverfasser: Vakhrusheva, V.S., Hruzin, N.V., Malykhin, D.G.
Format: Artikel
Sprache:English
Veröffentlicht: Національний науковий центр «Харківський фізико-технічний інститут» НАН України 2019
Schriftenreihe:Вопросы атомной науки и техники
Schlagworte:
Online Zugang:http://dspace.nbuv.gov.ua/handle/123456789/195226
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:Digital Library of Periodicals of National Academy of Sciences of Ukraine
Zitieren:Features of formation of crystallographic texture and properties in Ti-3Al-2.5V titanium alloy during tubes manufacture / V.S. Vakhrusheva, N.V. Hruzin, D.G. Malykhin // Problems of atomic science and technology. — 2019. — № 5. — С. 105-112. — Бібліогр.: 10 назв. — англ.

Institution

Digital Library of Periodicals of National Academy of Sciences of Ukraine
Beschreibung
Zusammenfassung:Texture formation processes at all technological stages of tube manufacture were considered. It has been established that at the stage of hot deformation and manufacture of TREX tubes, tangential and radial textures are formed, a large share of tangential component of the texture. Influence of main factors of the technological process on formation of texture and properties was established. Conditions for formation of a maximum amount of radial texture in tubes which ensure improvement of service properties of tubes were determined. To create maximum amount of radial texture in tubes, total reduction rate in passes and the wall to diameter reduction ratio (factor Q) are important. The reduction rate should be increased, especially in the last passes, to 75…85%. Heat treatment (stress relief annealing) practically does not change the tube texture.