Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments
In this paper changes in the proportions of certain microconstituents in the structure of weld metal and the heat affected zone are described and the mechanical and technological properties of welded joints of high-strength microalloyed Nb/Ti steel performed by E-process and MAG-process of welding w...
Gespeichert in:
| Datum: | 2010 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2010
|
| Schriftenreihe: | Фізико-хімічна механіка матеріалів |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/31751 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments / N. Bajic, V. Sijacki-Zeravcic, M. Rakin, K. Kovacevic // Фізико-хімічна механіка матеріалів. — 2010. — Т. 46, № 1. — С. 110-117. — Бібліогр.: 5 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| id |
irk-123456789-31751 |
|---|---|
| record_format |
dspace |
| spelling |
irk-123456789-317512012-03-18T12:09:08Z Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments Bajic, N. Sijacki-Zeravcic, V. Rakin, M. Kovacevic, K. In this paper changes in the proportions of certain microconstituents in the structure of weld metal and the heat affected zone are described and the mechanical and technological properties of welded joints of high-strength microalloyed Nb/Ti steel performed by E-process and MAG-process of welding with modification of the filler composition and welding parameters were analysed. The influence of different structures of filler material and welding parameters on the microstructure of HAZ and weld metal is studied with the aim to explain changes of mechanical and technological properties of welded microalloyed Nb/Ti steel joints. Описано зміни в пропорціях між певними складниками мікроструктури металу зварного шва і зони термічного впливу; проаналізовано механічні та технологічні параметри зварних з’єднань високоміцної мікролегованої Nb/Ti сталі, виконаних за різних технологій зварювання з модифікацією складу наповнювача і параметрів зварювання. Вивчено вплив структури матеріалу наповнювача і параметрів зварювання на мікроструктуру зварних з’єднань для пояснення їх механічних і технологічних властивостей. Описаны изменения в пропорциях между некоторыми составляющими микроструктуры металла сварного шва и зоны термического влияния; проанализированы механические и технологические параметры сварных соединений высокопрочной микролегированной Nb/Ti стали, выполненных в условиях разных технологий сварки с модификацией состава наполнителя и параметров сварки. Изучено влияние структуры материала наполнителя и параметров сварки на микроструктуру сварных соединений для объяснения их механических и технологических свойств. 2010 Article Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments / N. Bajic, V. Sijacki-Zeravcic, M. Rakin, K. Kovacevic // Фізико-хімічна механіка матеріалів. — 2010. — Т. 46, № 1. — С. 110-117. — Бібліогр.: 5 назв. — англ. 0430-6252 http://dspace.nbuv.gov.ua/handle/123456789/31751 en Фізико-хімічна механіка матеріалів Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| institution |
Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| collection |
DSpace DC |
| language |
English |
| description |
In this paper changes in the proportions of certain microconstituents in the structure of weld metal and the heat affected zone are described and the mechanical and technological properties of welded joints of high-strength microalloyed Nb/Ti steel performed by E-process and MAG-process of welding with modification of the filler composition and welding parameters were analysed. The influence of different structures of filler material and welding parameters on the microstructure of HAZ and weld metal is studied with the aim to explain changes of mechanical and technological properties of welded microalloyed Nb/Ti steel joints. |
| format |
Article |
| author |
Bajic, N. Sijacki-Zeravcic, V. Rakin, M. Kovacevic, K. |
| spellingShingle |
Bajic, N. Sijacki-Zeravcic, V. Rakin, M. Kovacevic, K. Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments Фізико-хімічна механіка матеріалів |
| author_facet |
Bajic, N. Sijacki-Zeravcic, V. Rakin, M. Kovacevic, K. |
| author_sort |
Bajic, N. |
| title |
Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments |
| title_short |
Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments |
| title_full |
Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments |
| title_fullStr |
Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments |
| title_full_unstemmed |
Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments |
| title_sort |
effect of welding regime and filler content on structure of microalloyed nb/ti steel weldments |
| publisher |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України |
| publishDate |
2010 |
| url |
http://dspace.nbuv.gov.ua/handle/123456789/31751 |
| citation_txt |
Effect of welding regime and filler content on structure of microalloyed Nb/Ti steel weldments / N. Bajic, V. Sijacki-Zeravcic, M. Rakin, K. Kovacevic // Фізико-хімічна механіка матеріалів. — 2010. — Т. 46, № 1. — С. 110-117. — Бібліогр.: 5 назв. — англ. |
| series |
Фізико-хімічна механіка матеріалів |
| work_keys_str_mv |
AT bajicn effectofweldingregimeandfillercontentonstructureofmicroalloyednbtisteelweldments AT sijackizeravcicv effectofweldingregimeandfillercontentonstructureofmicroalloyednbtisteelweldments AT rakinm effectofweldingregimeandfillercontentonstructureofmicroalloyednbtisteelweldments AT kovacevick effectofweldingregimeandfillercontentonstructureofmicroalloyednbtisteelweldments |
| first_indexed |
2025-07-03T12:12:48Z |
| last_indexed |
2025-07-03T12:12:48Z |
| _version_ |
1836627807682166784 |
| fulltext |
110
Ô³çèêî-õ³ì³÷íà ìåõàí³êà ìàòåð³àë³â. – 2010. – ¹ 1. – Physicochemical Mechanics of Materials
EFFECT OF WELDING REGIME AND FILLER CONTENT
ON STRUCTURE OF MICROALLOYED Nb/Ti STEEL WELDMENTS
N. BAJIC 1, V. SIJACKI-ZERAVCIC 2, M. RAKIN 3, K. KOVACEVIC 4
1 IHIS Research and Development Center, Belgrade, Serbia;
2 Faculty of Mechanical Engineering, Belgrade, Serbia;
3 Faculty of Technology and Metallurgy, Belgrade, Serbia;
4 Institute of Ferrous Metallurgy, Niksic, Montenegro
In this paper changes in the proportions of certain microconstituents in the structure of weld
metal and the heat affected zone are described and the mechanical and technological pro-
perties of welded joints of high-strength microalloyed Nb/Ti steel performed by E-process
and MAG-process of welding with modification of the filler composition and welding pa-
rameters were analysed. The influence of different structures of filler material and welding
parameters on the microstructure of HAZ and weld metal is studied with the aim to explain
changes of mechanical and technological properties of welded microalloyed Nb/Ti steel joints.
Key words: microalloyed steels, weld metal, heat affected zone, thermomechanical pro-
cessing, microstructure.
Depending on quality, microalloyed steels for X-grade wires can be alloyed
with Nb, V or Ti, or a combination of the three. Main property of microalloyed
steels is a fine-grain ferrite structure with grain size up to No13 according to the
ASTM standard. As it is well known, mechanical and technological properties of
welded joints are directly related to both chemical composition of the filler and
structure of the weld metal (WM) and heat-affected zone (HAZ). The microstruc-
ture of welded joints of fine-grain microalloyed steels consists of three basic ferrite
modifications: acicular ferrite, primary ferrite and Windmanstatten ferrite, origina-
ting as a result of different mechanisms of transformation and differently affecting
strength and ductility of a welded joint. Besides, small size of acicular ferrite grains
and presence of high-carbon boundaries also ensure maximum resistance to crack
initiation [1, 2]. By applying different welding technologies and post-weld heat
treatment methods, it is possible to obtain a whole spectrum of different structures
in HAZ and WM, which means a series of properties in the same fine-grain micro-
alloyed steel and also changes of mechanical and technological properties of the
welded joints. Therefore the aim of this work was to determine an optimum combi-
nation of composition of the filler and welding parameters to achieve the highest
possible values of tensile strength and toughness of the welded microalloyed Nb/Ti
steel joints using the welding E- and MAG-processes.
Materials and welding processes. Experimental welding of prepared speci-
mens – plates made of microalloyed Nb/Ti steels was carried out using two wel-
ding processes: MAG-process and E-process, where welding parameters were mo-
dified on two levels.
MAG (Metal Active Gas) is a welding process which uses consumable elec-
trode wire in an active shielding gas, CO2 or its mixtures with inert gases (argon,
Corresponding author: M. RAKIN, e-mail: marko@tmf.bg.ac.rs
111
helium) are most commonly used. The electrode wire can be a classical solid wire
or a powder filled wire. The latest type of this wire is produced under the name
“activated” filled wire which differs from the classical wires by the type of compo-
nents that are included in the composition of the core and the chemical composition
of the metal casing. Welding with filled electrode wire is characterized by a series
of techno-economic advantages compared to classical solid wire welding.
E-process welding is carried out with the coated electrode consisting of a me-
tallic core and a casing composed of various powdered ingredients (carbonates,
oxides, fluorides, alloying elements, etc.). By electrode melting during welding a
part of casing turn into a liquid slag, which as a protective layer covers the droplets
of melted metal and weld metal, while the other part of the electrodes casing
transforms into gases that surround and protect the area of the electric arc and
molten metal in the welding area from the surrounding air.
For E-process the quantity of the input heat was E1 = 7.5 kJ/cm and E2 =
= 21 kJ/cm, while the quantity of input heat in MAG-process was somewhat lower:
E1 = 7.3 kJ/cm, E2 = 18.5 kJ/cm.
Base metal. For the realization of experimental work the specimens of hot-
rolled thermo-mechanically processed steel bands made of Nb/Ti microalloyed
steel were chosen (according to API-5L designations they were as follows: A
(X52), B (X60) and C (X60), 7 and 12.5 mm thick, in which titanium content was
constant (0.011...0.013%); manganese content ranged from 1.182 to 1.375%, while
niobium content varied between 0.014 and 0.035% [3]. Batch designations, band
thickness and chemical composition of chosen grades of microalloyed steel are
given in Table 1. The results of testing (average values) of mechanical and techno-
logical properties of the base metal bands in the direction perpendicular to the
direction of rolling, as well as a calculated value of carbon equivalent Ceqv
(according to the International Institute of Welding) are given in Table 2.
Table 1. Chemical composition of microalloyed Nb/Ti steels
Chemical elements (mass.%) Steel
grade
Desig-
nation
Thick.,
mm C Si Mn P S Al Cu Nb Ti
Nb/Ti A 12.5 0.071 0.160 1.375 0.009 0.005 0.036 0.037 0.014 0.012
Nb/Ti B 7.0 0.053 0.264 1.182 0.020 0.006 0.031 0.018 0.027 0.011
Nb/Ti C 7.0 0.065 0.261 1.360 0.020 0.007 0.028 0.049 0.035 0.013
Table 2. Mechanical and technological properties and calculated value of Ceqv
Toughness (Charpy energy) KV, J Steel
grade
Re,
MPa
Rm,
MPa
A,
% +20°C –40°C –60°C
Ceqv
Nb/Ti–A 427 496 42 166 158 126 0.302
Nb/Ti–B 499 560 32 146 142 127 0.251
Nb/Ti–C 489 550 25 127 123 101 0.295
Re – yield stress; Rm – ultimate tensile strength; Ceqv = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15.
Filler metal. For welding of experimental specimens in E-process, four metal-
lurgical grades of coated electrodes were chosen: 1 – EVB Ni Mo (of NM1 designa-
tion), alloyed with Ni and Mo, with alkaline coating of 4 mm dia; 2 – ELE 53 B Ni
(of N1 designation), alloyed with Ni, with alkaline coating of 3.25 mm dia; 3 –
PIVA 255 B Mo Ni (of NM2 designation), alloyed with Ni and Mo of 4 mm dia;
4 – PIVA 255 B (of N2 designation), alloyed with Ni of 3.25 mm dia.
112
For welding of the specimens in MAG-process three grades of electrode wires
were chosen: 1 – PIVA 60 Ni (of W2 designation), alloyed with Ni of 1.2 mm dia;
2 – PIVA 60 (of W1 designation), alloyed with Ni of 1.2 mm dia; 3 – filled activa-
ted wire SW-10 (of FW designation), alloyed with Ti of 1.2 mm dia. The designa-
tions of coated electrodes and electrode wires as well as chemical composition and
mechanical properties of the weld metal for each grade of the filler material
separately are given in Table 3.
Table 3. Designation of used filler materials and WM properties
Chemical composition of WM, % Mechanical properties of WM Desig-
nat. C Si Mn Ni Mo Re, MPa Rm, MPa KV, J (–40°C)
NM1 0.06 0.40 0.90 1.10 0.35 > 520 640–710 > 125
NM2 0.08 0.5 0.95 2.50 0.35 550–640 650–750 60–90
N1 0.06 0.5 0.90 1.10 – > 460 570–650 > 47
N2 0.06 0.35 0.95 2.70 – 510–590 590–610 8 (–20)
W1 0.06–0.13 0.8–1.0 1.4–1.6 – – 410–490 510–590 80–125
W2 0.08–0.10 0.7–1.0 1.4–1.6 1.0–1.2 – 450–510 550–650 80–120
FW 0.08 0.50 1.50 – < 0.35Ti 600 700 120–160
Experimental welding. The preparation of the specimens for experimental
welding was carried out by cutting the hot-rolled steel bands with the longer side in
the direction of rolling, so that the outer dimensions of all specimens were the same
(400 by 125 mm). The notch was prepared by finishing the specimen edges at an
angles of 30° (for MAG-process) and 45° (for E-process), respectively [4].
The experimental welding of prepared specimens was performed using the
MAG-device and the device for welding in E-process. The welding process tempe-
rature was controlled by means of a contact thermometer in order to maintain it for
all welding passes at 100°C. Experimental welding was carried out without the base
metal preheating, as the calculated values of Ceqv were below the allowable limit
for all grades of microalloyed steels. The number of passes during the process of
welding depended on anticipated heat input that was varied on two levels. Experi-
mental welding was carried out on 12 pairs of steel plates by applying: MAG-pro-
cess with three grades of filler (W1, W2, FW) and in 3 (W1, FW) and 4 (W2) pas-
ses and E-process with four electrode grades (N1, N2, NM1, NM2) in 3 and 4 passes.
The analysis of the test results. Microstructural analysis of the weld metal.
Using the light microscope, the microstructure of the weld metal was observed in
the last pass of welded joints of Nb/Ti steels of A and B quality, obtained using
E-process of welding with filler metals of N1, NM1 and N2, NM2 quality with two
levels of heat input. Microphotographs of characteristic structural spots are given in
Fig. 1. In the WM of all presented welded joints the presence of various morpholo-
gical forms of ferrite was observed according to [5]. Most frequently present is
acicular ferrite (AF), followed by the secondary-phase containing ferrite (FS) and
Widmanstatten ferrite (WF).
The results of microstructure analysis of the weld metal are shown in Table 4.
The WM microstructure obtained with the N1 electrode in Nb/Ti steel (A de-
signation) and low-heat input consists of acicular ferrite (75…77%), while the rest
of it consisted of primary (PF) and secondary (FS) ferrite distributed along the
former austenite grain boundaries (Fig. 1a). For the same steel (Nb/Ti-A) in the WM
microstructure obtained using NM1 electrode, 78…82% of AF was found, while
113
the rest of it consisted of FS + PF (Fig. 1b). By comparison of the microstructural
properties of the WM obtained using the electrodes of different quality (N1 and
NM1) with the same base metal, band thickness and almost the same quantity of
input heat (E1 = 8.6 kJ/cm and E2 = 9.1 kJ/cm), one can conclude that with the elec-
trode of N1 quality a higher quantity of acicular ferrite (78…82%) was obtained
than in case of welding with NM1-electrode (75…77%). Supposing that the welded
joints were cooled at approximate cooling rates, a certain decrease of the AF por-
tion can be correlated to the molybdenum present in the NM1-electrode. The micro-
structure of the WM obtained with the N2-electrode in Nb/Ti-grade steel B (low
heat input) consisted of 56…58% of AF, while the rest consisted of FS + PF + WF
(Fig. 1c). Primary ferrite was isolated as fine-grain and coarse-grain, while WF was
rather coarse. At higher heat input, the structure consisted of ∼50% of AF (Fig. 1d),
while the rest mostly consisted of fine-grain primary ferrite with small portion of FS.
Fig. 1. WM microstructure in last pass of welded steels Nb/Ti (A, B) obtained with E-process
using fillers N1, NM1, N2 and NM2: a – steel-A, FM-N1, E = 8.6 kJ/cm; b – steel-A,
FM-NM1, E = 9.1 kJ/cm; c – steel-B, FM-N2, E = 11.5 kJ/cm; d – steel-B, FM-NM2,
E = 7.5 kJ/cm; e – steel-B, FM-N2, E = 18.5 kJ/cm; f – steel-B, FM-NM2, E = 21 kJ/cm.
Table 4. Results of microstructure analysis of weld metal specimens
Steel Nb/Ti-A Nb/Ti-B
WM N1 NM1 N2 N2 NM2 NM2
Arc
Energy
E1 = 8.6
kJ/cm
E1 = 9.0
kJ/cm
E1 = 11.5
kJ/cm
E2 = 18.5
kJ/cm
E1 = 7.5
kJ/cm
E2 = 21
kJ/cm
Micro-
structure
78…82% AF
Rest
PF + FS
75…77% AF
Rest
PF + FS
56…58% AF
Rest
PF + FS + WS
∼50% AF
Rest
PF + FS
72% AF
Rest
PF + FS
70% AF
Rest
PF + FS
Fig. 1a 1b 1c 1d 1e 1f
With welded joints made of the same base metal (Nb/Ti-B), with the same N2
electrode and the same band thickness but different heat input, somewhat different
morphological characteristics of the WM were obtained – related both to quantity
and grain size of different ferrite modifications. Higher heat input favoured forma-
tion of a smaller quantity of AF, but of higher grain fineness. The microstructure in
the last pass, made using the NM2 electrode in Nb/Ti-B steel with low heat input,
consisted of AF (∼72%) and PF + FS isolated on grain boundaries (Fig. 1e). The
114
structure of the WM obtained with a higher heat input, and other welding parame-
ters unmodified, consisted of a reduced AF portion (∼70%) and increased PF and
also of lower FS portion, which is illustrated in Fig. 1f. Varied heat input in case of
welding of Nb/Ti-B steel with NM2 electrode and with the same band thickness
also resulted in somewhat varied quantities of AF.
The weld metal microstructure of Nb/Ti-A steel specimen made of electrode
W2 wire consists of AF (∼55%), while the rest consists of coarse-grain, locally
even block-type, PF with small quantity of FS (Fig. 2a). The same steel grade
welded with filled wire in the WM contains ∼68% of AF, while the rest consists of
coarse-grain PF with FS in traces (Fig. 2b).
The weld metal of Nb/Ti-B steel specimen made with filled wire and two diffe-
rent heat inputs showed different fraction and grain fineness of morphological fer-
rite forms. In the WM obtained with a lower heat input (Fig. 2c) AF was present in
the quantity of ~65%, while the rest consisted of fine-grain uniformly distributed PF.
The microstructure of the WM obtained with higher heat input consisted of 45…50%
of AF, very coarse and here and there block-type PF, WF and FS in traces (Fig. 2d).
By welding with filled wire FW the largest quantity of AF was obtained (∼78…
80%), while the rest consisted of very fine PF and FS. The reason for a larger share
of AF in the weld metal structure is explained by the influence of the composition of
the activator and microalloying elements in the core composition of the filled wire.
Fig. 2. WM microstructure in the last pass of welded
Nb/Ti steels (A, C) obtained with MAG-process using
wire (W1, W2) and filled wire (FW): a – steel-A, D-W2;
E = 8.4 kJ/cm; b – steel-A, DM-FW; E = 9.0 kJ/cm;
c – steel-C, DM-W1, E = 6.3 kJ/cm;
d – steel-C, DM-FW, E = 8.8 kJ/cm.
Microstructural analysis of HAZ. The microstructure of Nb/Ti steel (A, B, C)
consists of fine-grain ferrite and pearlite. Scanning electronic microscope (SEM)
analysis of HAZ structure was carried out on Nb/Ti steel, A (Fig. 3) and B (Fig. 4)
quality from BM to WM, which means that all zones in HAZ were included. On
microphotographs of Nb/Ti steel (A) one can observe a fine-grain ferrite/pearlite
structure of the BM (Fig. 3a, b) and the appearance of the structure in the zone of
normalization (Fig. 3c, d); the microphotographs in Fig. 3e, f show a part of the
structure in the overheated zone of HAZ (a part of the WM structure can be seen up
to the fusion line). SEM microphotographs (Fig. 4a–d) show the HAZ structure up
to the fusion line for the joints made with two levels of heat input (E1 = 7.5 kJ/cm
and E2 = 21 kJ/cm) for Nb/Ti steel (B quality). One can see that with the specimens
of welded joints made with higher heat input the HAZ structure in the zones of
normalization and overheating is coarser than the HAZ structure of welded joints
made with lower heat input (Fig. 4a–c).
115
Fig. 3. SEM microphotographs of different zones of microstructure of welded steel Nb/Ti-A:
a – base metal (ferrite + pearlite); b – magnification of photograph a; c – zone of normalization;
d – magnification of photograph c; e – WM zone; f – magnification of photograph e.
Fig. 4. HAZ microstructure of welded steel Nb/Ti-B: a–c – E1 = 7.5 kJ/cm; d–f – E2 = 21 kJ/cm.
SEM microphotographs (Fig. 4a–d) show the HAZ structure up to the fusion line
for the joints made with two levels of heat input (E1 = 7.5 kJ/cm and E2 = 21 kJ/cm)
for Nb/Ti steel (B). One can see that for the specimens of welded joints made with
higher heat input the HAZ structure in the zones of normalization and overheating is
coarser than the that of welded joints made with lower heat input (Fig. 4a–c). The SEM
analysis of the HAZ structure of Nb/Ti-B steel made with low heat input (7.5 kJ/cm)
demonstrated that the fine-grain structure was obtained in the overheated zone.
Analysis of mechanical properties of welded joints. Testing results of tensile
strength of welded microalloyed steel specimens (quality Nb/Ti) are shown in com-
parison with tensile strength values of the base metal in the chart, Fig. 5. Compari-
son of testing results of tensile strength of the welded joints and the base metal
Nb/Ti steel indicates that for steel marked (A) the highest values were achieved in
specimens welded with an electrode (1.1% Ni, 0.35% Mo) EVB Ni Mo while spe-
cimens welded with N1 and W2 have lower values but still higher than tensile
strength values of the base metal, and steel (B) has tensile strength of welded joints
much higher than that of the base metal for both electrode qualities; NM2 alloyed
with nickel and molybdenum (2.5% Ni, 0.35% Mo), PIVA 253B Mo and N2
alloyed with 2.7% Ni (PIVA 255 B). Steel (C) has tensile strength of welded joints
much higher than that of the base metal. On the basis of tensile strength analysis in
116
welded joints the conclusion is done that the best results have been achieved with
electrodes NM2, N2 and electrode wires W1, FW.
Toughness analysis on the Charpy
pendulum. Change in toughness depen-
ding on testing temperature for weld
metal and HAZ (base metal B), carried
out with E-process and electrode NM2
(2.5% Ni + 0.35% Mo) with two levels
of heat input (E1 = 7.5 kJ/cm, E2 = 21
kJ/cm) is shown in Fig. 6a, where tough-
ness increase has been detected in HAZ
with lower heat input during welding,
while the toughness values of weld metal
at lower temperatures are much higher
than of those in HAZ because of the
content of Ni and Mo in the weld metal.
Toughness vs. temperature depen-
dence of welded joints (base metal C),
carried out with MAG process with
electrode wire W1 (1.5% Mn) and two
levels of heat input (E1 = 6.3 kJ/cm, E2 = 15.5 kJ/cm) is shown in Fig. 6b, where
there is a large difference between toughness of the weld metal and the HAZ but no
difference in toughness for the two mentioned levels of heat input.
Fig. 6. Dependences of Charpy energy
on testing temperature for weld metal
and HAZ: a – steel Nb/Ti (B);
b, c – steel Nb/Ti (C): ♦ – B-WM (E2);
■ – B-HAZ (E2); ▲ – B-WM (E1);
× – B-HAZ (E1).
Toughness change subject to testing temperature in HAZ and weld metal
carried out in MAG process with filled wire FW-10 (0.35% Ti) on the base metal
Nb/Ti (C) and one level of heat input (E = 8.8 kJ/cm) is shown in Fig. 6c, and there
is a large difference between toughness values in the HAZ and the weld metal.
CONCLUSIONS
Based on the results obtained by experimental testing of the effects of filler
material and welding parameters on modification of the WM and HAZ structure of
fine-grain microalloyed steels, the following conclusions can be drawn.
Fig. 5. Compared values of tensile strength
of base metal and welded joints made by:
E-process with electrode quality NM1, NM2,
N1, N2; MAG-process with electrode wire
W1, W2, FW. Designations: A, B, C – steel
type Nb/Ti (X65); NM1, NM2, N1, N2 –
coated electrode; W1, W2 – classical
electrode wire; FW – filled wire.
117
– In the WM made in E-process with NM1 electrode in the last pass, AF por-
tion was approx. 75…77% and the rest consisted of PF and FS, while in the WM
made with NM2 electrode AF portion in the structure was 72% and the rest consis-
ted of PF and FS. The portion of AF in the WM made with N2 electrode was 56…
58% and it was significantly higher with N1 electrode (78…82%) that particularly
affected impact toughness.
– Formation of various quantities of acicular ferrite in the weld metal of wel-
ded joints, obtained using N1 and NM1 electrodes, can be attributed to very low
cooling rates rather than to molybdenum with which the NM1 electrode was
alloyed (Table 3), considering that all other variables such as base metal quality,
steel-band thickness and quantity of input heat were the same.
– The structure of the WM obtained in MAG-process with electrode wire W2
in the last pass contained 55…65% of AF and the rest consisted of PF and FS,
while in the WM made with FW the portion of AF in the structure was 78…80%
and the rest consisted of PF and FS. The quantity of AF is directly correlated to the
increase of WM toughness.
– Microstructural analysis of HAZ of tested welded joints made with two le-
vels of heat input (E1 = 7.5 kJ/cm and E2 = 21 kJ/cm) has shown that the structure
was finer with the lower level of heat input in the zone of normalization and over-
heating which is another significant factor in the technology planning and selection
of optimum welding regime of the above mentioned steel grades.
– In Nb/Ti steel, the best mechanical and technological properties of welded
joints were obtained after welding with NM2 electrode (2.5% Ni + 0.35% Mo)
with low heat input (7.5 kJ/cm).
РЕЗЮМЕ. Описано зміни в пропорціях між певними складниками мікроструктури
металу зварного шва і зони термічного впливу; проаналізовано механічні та технологічні
параметри зварних з’єднань високоміцної мікролегованої Nb/Ti сталі, виконаних за різних
технологій зварювання з модифікацією складу наповнювача і параметрів зварювання.
Вивчено вплив структури матеріалу наповнювача і параметрів зварювання на мікрострук-
туру зварних з’єднань для пояснення їх механічних і технологічних властивостей.
РЕЗЮМЕ. Описаны изменения в пропорциях между некоторыми составляющими
микроструктуры металла сварного шва и зоны термического влияния; проанализированы
механические и технологические параметры сварных соединений высокопрочной микро-
легированной Nb/Ti стали, выполненных в условиях разных технологий сварки с модифи-
кацией состава наполнителя и параметров сварки. Изучено влияние структуры материала
наполнителя и параметров сварки на микроструктуру сварных соединений для объясне-
ния их механических и технологических свойств.
Acknowledgements. This work is supported by the Serbian Ministry of
Science and Technological Development (project number 19061).
1. Precipitation Behavior and its Effect on Strengthening of an HSLA-Nb/Ti Steel / M. Char-
leux, W. J. Poole, M. Militzer and A. Deschamps // Metall. and Mater. Trans. A. – 2001.
– 32. – P. 1635–1647.
2. Effect of vanadium and niobium on the properties and microstructure of the intercritically re-
heated coarse grained heat affected zone in low carbon microalloyed steels / Y. Li, D. N. Crow-
ther, M. J. W. Green and P. S. Mitchell // ISIJ International. – 2001. – 41. – P. 46–55.
3. Bajić N. and Šijački-Žeravčić V. The analysis of change of structural and mechanical proper-
ties of welded joints of microalloyed NB/V steel grade by changing the composition of filler
material // Int. Conf. Weld. 2003. – Belgrade, 2003.
4. Bajić N. Analysis of the filler material and welding parameters influence on properties of
weld joints of new generation of high strength microalloyed steels (in Serbian), Ph D Disser-
tation, Faculty of Mechanical Engineering, Belgrade. – 2004.
5. Zhang Z. and Farrar R. A. An atlas of continuous cooling transformation (CCT) diagrams
applicable to low carbon low alloy weld metals. – London: The Institute of Materials, 1995.