Vacuum CVD coatings Ta on target W plate of neutrons source
The paper presents data on the creation of a tungsten target, protected from corrosion under irradiation with a power of up to 100 kW. A protective coating of tantalum with a thickness of 250 µm was deposited on the surface of tungsten plates 66x66 mm, thickness 10; 6; 4; 3 mm. The coating has a sol...
Gespeichert in:
| Datum: | 2019 |
|---|---|
| Hauptverfasser: | , , , , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Національний науковий центр «Харківський фізико-технічний інститут» НАН України
2019
|
| Schriftenreihe: | Вопросы атомной науки и техники |
| Schlagworte: | |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Vacuum CVD coatings Ta on target W plate of neutrons source / B.V. Borts, I.M. Neklyudov, Yu.I. Polyakov, S.G. Rudenky, Yu.V. Lukirsky, I.A. Vorobyov, А.А. Lopata // Problems of atomic science and technology. — 2019. — № 5. — С. 161-166. — Бібліогр.: 5 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| Zusammenfassung: | The paper presents data on the creation of a tungsten target, protected from corrosion under irradiation with a power of up to 100 kW. A protective coating of tantalum with a thickness of 250 µm was deposited on the surface of tungsten plates 66x66 mm, thickness 10; 6; 4; 3 mm. The coating has a solid-phase compound over the entire surface of tungsten and is hermetic. This was achieved by CVD (chemical vapor deposition) tantalum deposition in a vacuum of 2.66·10⁻² Pa on a plate surface heated to ~ 1700 K using the thermal dissociation reaction of tantalum pentachloride vapor. Such tungsten plates, equipped with tantalum coatings with desired properties, were used in the Neutron Source installation of the NSC KIPT. |
|---|