The influence of temperature on impact toughness and dynamic crack growth resistance of 25Kh1M1F steel

The influence of temperature on impact toughness and dynamic crack growth resistance of 25Kh1M1F steel

Gespeichert in:

Bibliographische Detailangaben
Datum:	2010
Hauptverfasser:	P. O. Marushchak, R. T. Bishchak, V. Hlikha, A. P. Sorochak
Format:	Artikel
Sprache:	English
Veröffentlicht:	2010
Schriftenreihe:	Materials Science (Physicochemical mechanics of materials)
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000657322
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

The influence of laser-impact treatment on impact toughness of heat-resistant steels
von: P. V. Yasnii, et al.
Veröffentlicht: (2010)

Prospects of use steel strengthened by VN for slab caster rollers instead of 25Kh1M1F steel
von: I. F. Kirchu, et al.
Veröffentlicht: (2015)

Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States
von: Zrilic, M., et al.
Veröffentlicht: (2004)

The influence of microstructure components on static crack growth resistance of 13KhMF steel
von: I. R. Dzioba
Veröffentlicht: (2011)

Impact toughness of bimetallic specimens cut out from the rolls of continuous casting machines with welded layer
von: P. O. Marushchak, et al.
Veröffentlicht: (2012)

Corrosion fatigue crack growth resistance of steel for boom sprayers frame
von: A. M. Syrotiuk, et al.
Veröffentlicht: (2020)

Determination of crack growth resistance characteristics of 17H1S steel under transversal shear
von: Ya. L. Ivanytskyi, et al.
Veröffentlicht: (2013)

Vacuum Activated Diffusion Chromium Plating of 15Kh12VNMF and 20Kh1M1F1TR Steels
von: S. G. Rudenki, et al.
Veröffentlicht: (2022)

Impact toughness of 34KhN2MA steel welded joints prepared by electrodes with different phase composition
von: A. R. Dziubyk
Veröffentlicht: (2020)

Strength and fatigue crack growth resistance of as-cast graphitic steels
von: I. M. Andreiko, et al.
Veröffentlicht: (2013)

Low-cycle fatigue and cracking resistance of power plant boiler pipes and steam lines of 12Kh1MF steel
von: Zelenskii, V.G., et al.
Veröffentlicht: (1985)

The influence of gas pipeline long-term operation on fatigue crack growth resistance of 17H1S steel
von: Ye. V. Kharchenko, et al.
Veröffentlicht: (2016)

Kinetics of growth of corrosion cracks in pipe steel 17G1S
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

The influence of hydrogenon static crack growth resistance of refractory steels
von: L. M. Ivaskevych, et al.
Veröffentlicht: (2012)

Fatigue crack growth resistance of steels of long-term exploited steam pipeline bends
von: O. P. Ostash, et al.
Veröffentlicht: (2012)

Computer analysis of surface morphology of 15Kh13MF steel after laser pulse treatment
von: P. O. Marushchak, et al.
Veröffentlicht: (2013)

Anisotropy of the mechanical properties of 15Kh1M1F degraded steel after its exploitation on HPP pipelines
von: O. Z. Student, et al.
Veröffentlicht: (2011)

Improvement of impact toughness of metal of combined welded joints of alloyed bainite steels
von: S. I. Moravetskij, et al.
Veröffentlicht: (2017)

The influence of thermal cycles work on degradation of heat-resistant steel properties
von: P. O. Marushchak, et al.
Veröffentlicht: (2010)

Develop¬ment of in-laboratory method of steel degradation for assessing their crack growth resistance
von: M. I. Hredil, et al.
Veröffentlicht: (2021)

Fatigue crack growth resistance characteristics of steels under transverse shear (Review)
von: T. M. Lenkovskyi
Veröffentlicht: (2014)

Delayer fracture resistance of welded joints of rotor steel 25Kh2NMFA after welding reheating
von: Ju. Skulskij, et al.
Veröffentlicht: (2019)

The influence of crack faces friction on fatigue crack growth resistance of 65H steel under transverse shear
von: T. M. Lenkovskyi
Veröffentlicht: (2014)

The influence of thermal treatment conditions on strength and fatigue crack growth resistance of 65H steel
von: O. P. Ostash, et al.
Veröffentlicht: (2018)

Fatigue crack propagation resistance of the operated welded joint of 17H1S pipe steel
von: V. A. Voloshyn
Veröffentlicht: (2020)

Fatigue crack growth resistance of long-term operated steel of the main oil pipeline
von: A. V. Bogdanovich, et al.
Veröffentlicht: (2011)

Diagnostics of the technical state of steam pipelines at TPP by hardness and crack growth resistance of steel
von: H. V. Krechkovska, et al.
Veröffentlicht: (2018)

Static crack growth resistance of 20 and 30CrMo steels in NACE solution
von: M. R. Chuchman
Veröffentlicht: (2016)

Pulsed barrier discharge for treatment of surfaces of 25KhHNMT steel plates
von: I. V. Bozhko, et al.
Veröffentlicht: (2023)

Temperature dependence of cracking resistance of 15KhSND steel and special features of its fracture. Report 2
von: Gol'dshtein, R.V., et al.
Veröffentlicht: (1985)

Assessment of steam pipeline steels degradation by impact toughness on the specimens with a cut of different-geometry
von: H. V. Krechkovska, et al.
Veröffentlicht: (2016)

Flexural Fracture Toughness and First-Crack Strength Tests of Steel Fiber-Silica Fume Concrete and Its Engineering Applications
von: Zhang, J.P., et al.
Veröffentlicht: (2018)

Prediction of crack growth resistance of cement stone and fibre
von: V. P. Sylovaniuk, et al.
Veröffentlicht: (2015)

Diagnostic of the surface of 20 and 17H1S-U steels corrosion damaged by sulfate reducing bacteria
von: M. S. Polutrenko, et al.
Veröffentlicht: (2020)

Dependence of the Critical Temperature Magnitude at Impact Toughness Tests on the Parameters of the Microstructure of Martensitic Low-Carbon Steels
von: S. O. Kotrechko, et al.
Veröffentlicht: (2014)

Diagnostics of serviceability of heat-resistance steel of metallurgical equipment after thermocycling
von: P. V. Yasnii, et al.
Veröffentlicht: (2011)

An Alternative Approach to the Fracture Toughness of Dual Phase Steels
von: S. Ulu, et al.
Veröffentlicht: (2013)

An Alternative Approach to the Fracture Toughness of Dual Phase Steels
von: Ulu, S., et al.
Veröffentlicht: (2013)

Service ability of 35KhF steel in hydrogen sulphide environments
von: H. V. Chumalo
Veröffentlicht: (2010)

Stress corrosion cracking of Kh70 pipe steel under cathode protection
von: L. I. Nyrkova
Veröffentlicht: (2020)