Evaluation of heat-power equipment resource under long-term static loading, high temperature and action of hydrogen

Evaluation of heat-power equipment resource under long-term static loading, high temperature and action of hydrogen

Gespeichert in:

Bibliographische Detailangaben
Datum:	2018
Hauptverfasser:	Chang Shu, O. V. Hembara, Ya. Chepil
Format:	Artikel
Sprache:	English
Veröffentlicht:	2018
Schriftenreihe:	Materials Science (Physicochemical mechanics of materials)
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000851338
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

The life-time of plates with cracks under the long-term static loading
von: Ye. Andreikiv, et al.
Veröffentlicht: (2012)

Determination of residual lifetime of the two-ply plates with a system of cracks under action of long-term static loading and high temperature
von: Ye. Andreikiv, et al.
Veröffentlicht: (2016)

Mathematical models for estimation of residual life-time of plates with cracks systems under actions of long duration static loading, high temperature and hydrogen
von: Ye. Andreikiv, et al.
Veröffentlicht: (2014)

Calculation model for assessment of fibroconcrete structures lifetime under long-term static loading
von: Ye. Andreikiv, et al.
Veröffentlicht: (2020)

Modeling of hydrogen effect on bearing capacity of structures of power equipment under temperature creep
von: F. Qin, et al.
Veröffentlicht: (2017)

Long-term durability of the thin-walled structural elements with the low-temperature creep cracks under static loading
von: Yu. Ya. Matviiv
Veröffentlicht: (2012)

Mathematical model for determination of life-time of plates with systems of cracks under long-term static breaking load and high temperature
von: Ye. Andreikiv, et al.
Veröffentlicht: (2012)

Application of energy approach to the evaluation of serviceability of a steam boiler drum under thermal cycling and hydrogenation
von: O. V. Hembara, et al.
Veröffentlicht: (2017)

Evaluation of life time of the power equipment elements with account of the operating environment effect
von: Ya. L. Ivanytskyi, et al.
Veröffentlicht: (2015)

Correlation dependences between short-term/long-term static strength characteristics and creep resistance of tungsten at high temperatures
von: Borisenko, V.A., et al.
Veröffentlicht: (2005)

Control of technical condition of technological equipment of petroleum-processing productions in long-term service in hydrogen-containing working environment
von: V. O. Stryzhalo, et al.
Veröffentlicht: (2021)

Fractographic signs of gigacycle fatigue and hydrogenation under long-term operating heat-resistant steels
von: O. D. Smiian, et al.
Veröffentlicht: (2020)

Influence of oxygen diffusion saturation on the fatigue and long-term static strength of titanium alloys
von: V. M. Fedirko, et al.
Veröffentlicht: (2014)

Equipment for low temperature and freeze-drying preservation, long-term storage of biological materials
von: V. N. Batrakov, et al.
Veröffentlicht: (2008)

Experimental and Theoretical Design Methodology of Hemispherical Shells under Extreme Static Loading
von: Galiev, Sh.U., et al.
Veröffentlicht: (2004)

The influence of sampling options on accuracy of numerical solution of the three-dimensional problem of hydrogen diffusion
von: O. V. Hembara, et al.
Veröffentlicht: (2016)

Creep crack growth in structuralelements under long-term loading
von: Ye. Andreikiv, et al.
Veröffentlicht: (2012)

Modelling of the structural elements deformation under conditions of creep, stress corrosion cracking and hydrogenation
von: O. V. Hembara, et al.
Veröffentlicht: (2021)

Finite element simulation of hydrogen influence on the accumulation of damages in the steels under high-temperature creep
von: Jiang Qiongqin, et al.
Veröffentlicht: (2019)

Computer modeling of the influence of hydrogen saturation on the durability of pipe elements
von: Ming Wei, et al.
Veröffentlicht: (2021)

Complex application of the method of acoustic emission and energy approach to determine the residual life of a structure under effect of long-term static load, corrosion and material degradation
von: O. Y. Andreikiv, et al.
Veröffentlicht: (2024)

Failure of organic glass after alternating long-term and cyclic loading
von: Arutyunyan, R.A., et al.
Veröffentlicht: (1985)

Durability of Thermo-Elastohereditary Bodies under Long-Term Cyclic Loading
von: A. F. Bulat, et al.
Veröffentlicht: (2019)

The influence of temperature and cyclic loading on hydrogen embrittlement of nickel heat-resistant alloys
von: L. M. Ivaskevych
Veröffentlicht: (2011)

Labor safety during operation of machines operating at long-term cyclic loads
von: V. I. Dyrda, et al.
Veröffentlicht: (2019)

On starting loads of equipment operating at high temperatures
von: Ja. Nedoseka, et al.
Veröffentlicht: (2012)

Prediction of the long-term strength heat-resistant nickel alloy
von: V. V. Krivenjuk
Veröffentlicht: (2009)

On the problem of long-term service life prediction of creep rupture strength for the metal in power equipment
von: V. V. Krivenjuk, et al.
Veröffentlicht: (2014)

Evaluation of the Long-Term Strategic Opportunities for Enhancing the Competitiveness of Ukrainian Products
von: V. I. Ljashevskaja
Veröffentlicht: (2015)

Electrochemical methods of evaluation of degradation of long-term operation structural steels
von: O. I. Zvirko
Veröffentlicht: (2016)

Present problems of vibration isolation in heavy mining machines at long-term cyclic loads
von: V. I. Dyrda, et al.
Veröffentlicht: (2021)

Present problems of vibration isolation in heavy mining machines at long-term cyclic loads
von: V. Dyrda, et al.
Veröffentlicht: (2020)

Thermomechanical stability of elastomer elements of heavy vibromachines under long-term cyclic loading
von: V. I. Dyrda, et al.
Veröffentlicht: (2017)

Problems and prospects of long-term planning in the heat supply sector of Ukraine
von: H. H. Heletukha, et al.
Veröffentlicht: (2019)

Long-Term Aging Effect on the Crack Growth in the of Main Circulating Pump Casing Material
von: Xue, F., et al.
Veröffentlicht: (2015)

Application of the method of complex forecasting for the determination of long-term demand for energy resources
von: M. M. Kulyk, et al.
Veröffentlicht: (2017)

Evaluation of hydrogen concentration in the process zone at the crack tip
von: Ya. L. Ivanytskyi, et al.
Veröffentlicht: (2010)

Karyotype alterations in human lung adenocarcinoma cells after long-term action of interferon-alpha
von: Kovaleva, O.A., et al.
Veröffentlicht: (2010)

Computer modeling of deformation of structural elements in creep conditions under metal hydrogenation and complex loading
von: J. Congyuan, et al.
Veröffentlicht: (2021)

Monitoring the technical condition of process piping at long-term operation in hydrogen-containing working medium
von: S. Z. Stasiuk
Veröffentlicht: (2018)