Methodology of numerical prediction of serviceability of pipeline elements with corrosion-erosion defects under conditions of high-temperature operation

Methodology of numerical prediction of serviceability of pipeline elements with corrosion-erosion defects under conditions of high-temperature operation

Gespeichert in:

Bibliographische Detailangaben
Datum:	2017
Hauptverfasser:	A. S. Milenin, E. A. Velikoivanenko, G. F. Rozynka, N. I. Pivtorak
Format:	Artikel
Sprache:	English
Veröffentlicht:	2017
Schriftenreihe:	Technical diagnostics and non-destructive testing
Online Zugang:	http://jnas.nbuv.gov.ua/article/UJRN-0000818450
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!
Назва журналу:	Library portal of National Academy of Sciences of Ukraine \| LibNAS

Institution

Library portal of National Academy of Sciences of Ukraine | LibNAS

Ähnliche Einträge

Numerical methodology of prediction of the reliability and residual life of welded pipeline elements with corrosion-erosion defects
von: O. S. Milenin, et al.
Veröffentlicht: (2020)

Prediction of residual strength of pipeline elements with detected corrosion defects based on Monte-Carlo method
von: A. S. Milenin, et al.
Veröffentlicht: (2019)

Numerical prediction of effectiveness of reinforcement of defective pipelines by composite material bands
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2016)

Probabilistic estimate of the condition of pipeline elements with detected thinning defects
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2014)

High-performance methods of numerical studies for solving the problems of evaluation of defective structure serviceability
von: A. S. Milenin, et al.
Veröffentlicht: (2018)

Evaluation of serviceability of main pipeline with a local thinning of wall in arc surfacing repair
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2015)

Simulation of processes of initiation and propagation of subcritical damage of metal in welded pipeline elements at low-cycle loading
von: E. A. Velikoivanenko, et al.
Veröffentlicht: (2016)

Numerical analysis of the features of limiting state of welded pipeline elements under ultra-low-cycle loading
von: O. V. Makhnenko, et al.
Veröffentlicht: (2021)

Prediction of Flow Accelerated Corrosion of NPP Pipeline Elements by Network Simulation Method
von: Biblik, Irina V., et al.
Veröffentlicht: (2018)

Prediction of Flow Accelerated Corrosion of NPP Pipeline Elements by Network Simulation Method
von: Biblik, I.V., et al.
Veröffentlicht: (2018)

Prediction of Flow Accelerated Corrosion of NPP Pipeline Elements by Network Simulation Method
von: I. V. Biblik, et al.
Veröffentlicht: (2018)

Prediction of Flow Accelerated Corrosion of NPP Pipeline Elements by Network Simulation Method
von: Biblik, Irina V., et al.
Veröffentlicht: (2018)

Procedure of ranging corrosion defects of the main gas pipelines found at in-pipe diagnostics
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)

Assessment of serviceability of long-term operating oil pipelines by the parameters of their defectiveness
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2013)

Numerical assessment of brittle strength of field welds of the main gas pipelines at transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2023)

Development of procedure for determination of wall thickness in NPP pipeline at erosion-corrosion wear of material
von: I. V. Oryniak, et al.
Veröffentlicht: (2017)

Evaluation of serviceability of pipeline of the first contour of WWR-M reactor with defects in welded joints
von: O. V. Makhnenko, et al.
Veröffentlicht: (2015)

Analysis of conditions of initiation and propagation of corrosion cracks in the zone of circumferential joints of main gas pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2009)

Mathematical modeling of local corrosion element in pipelines with galvanic couple operating in soil conditions
von: Stepova, O.V., et al.
Veröffentlicht: (2016)

Numerical analysis of the regularities of the infuence of pipe steel degradation on the reliability of corroded main gas pipelines used for transportation of gas-hydrogen mixtures
von: O. S. Milenin, et al.
Veröffentlicht: (2024)

Mathematical modeling of local corrosion element in pipelines at galvanic couple's operation in soil conditions
von: O. V. Stepova, et al.
Veröffentlicht: (2016)

Tubing of high corrosion resistance and operational reliability for severe corrosion-erosion conditions of oil and gas production
von: V. I. Bolshakov, et al.
Veröffentlicht: (2017)

Mutual influence of defects in welded joint zone at different force loading
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Permissible pressure for filler of sealed sleeves used to repair main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2011)

Improvement of method of assessment of risk of fracture in the zone of wall thinning in main pipelines
von: V. I. Makhnenko, et al.
Veröffentlicht: (2010)

Prediction of residual pipeline resource taking into account the operation loading conditions
von: Banahevych, Yu.V., et al.
Veröffentlicht: (2009)

Risk of failure during thinning of wall of main pipeline in the area of circumferential welded joints at the presence of bending moments along the axis of pipeline
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Corrosion degradation of long-term operated gas pipeline elbow with macrodefect
von: O. I. Zvirko, et al.
Veröffentlicht: (2016)

Evaluation of fracture kinetics of operated gas pipeline elements
von: Ye. I. Kryzhanivskyi, et al.
Veröffentlicht: (2015)

Features of analysis of the technical state and support of reliability of the main gas pipelines at transportation of gashydrogen mixtures (Review)
von: O. S. Milenin, et al.
Veröffentlicht: (2022)

Account for pore formation in estimation of limiting state in the zone of pressure vessel wall thinning defect
von: V. I. Makhnenko, et al.
Veröffentlicht: (2012)

Mathematical Simulation of Lumped Elements Service of Main Gas Pipelines Linear Part
von: I. I. Ostapjuk
Veröffentlicht: (2012)

Peculiarities of application of split T-joints in repair and reconstruction of main pipelines under service conditions
von: V. S. But, et al.
Veröffentlicht: (2009)

Methodology of multiparametral diagnostics of technical condition of pipelines in long-term operation
von: M. O. Karpash
Veröffentlicht: (2013)

Reinforcement of an NPP pipeline with a wall thinning defect by applying external weld ovelay
von: G. V. Vorona, et al.
Veröffentlicht: (2024)

Multiscale procedure of numerical assessment of damage rate and technical state of structures from fibrous materials
von: O. S. Milenin, et al.
Veröffentlicht: (2021)

A numerical method of multiscale modeling of the stress-strain state of large-sized sctructures in site welding
von: O. S. Milenin, et al.
Veröffentlicht: (2023)

Prediction of corrosion damage of oil and gas pipelines based on monitoring the structure and phase composition of gas-liquid flow from the well
von: P. M. Raiter
Veröffentlicht: (2012)

Corrosion of an internal wall of industrial gas pipeline
von: Yu. Kovalenko, et al.
Veröffentlicht: (2012)

Corrosive and Mechanical Degradation of Pipelines in Acid Soils
von: Poberezhnyi, L.Ya., et al.
Veröffentlicht: (2017)