Кореляція між фотолюмінесцентними та фотоелектричними властивостями ZnO, легованого Mn
ZnO ceramics undoped and doped with manganese are investigated. The Mn content NMn is varied from 1019 to 1021 cm−3. The photoluminescence (PL), diffuse reflection, and photoconductivity (PC) spectra are measured. The quenching of the self-activated ZnO emission and the appearance of the light absor...
Gespeichert in:
| Datum: | 2018 |
|---|---|
| Hauptverfasser: | , , , , , , |
| Format: | Artikel |
| Sprache: | English Ukrainian |
| Veröffentlicht: |
Publishing house "Academperiodika"
2018
|
| Schlagworte: | |
| Online Zugang: | https://ujp.bitp.kiev.ua/index.php/ujp/article/view/2018050 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Ukrainian Journal of Physics |
Institution
Ukrainian Journal of Physics| Zusammenfassung: | ZnO ceramics undoped and doped with manganese are investigated. The Mn content NMn is varied from 1019 to 1021 cm−3. The photoluminescence (PL), diffuse reflection, and photoconductivity (PC) spectra are measured. The quenching of the self-activated ZnO emission and the appearance of the light absorption and PC are observed in the same spectral region (400–600 nm) under the doping. Simultaneously, a week PL band peaked at 645 nm arose and was assigned to intra-shell transitions in Mn2+Zn centers. Based on the analysis of obtained results, the quenching effect is attributed to the re-absorption of the self-activated ZnO emission by Mn ions. A scheme of electron transitions that allows an explanation of the low intensity of the Mn-related emission is proposed. |
|---|