Deposition of borophosphosilicate glass films using the TEOS–dimethylphosphite–trimethylborate system
Modernization of horizontal low pressure deposition system has been performed. The liquid source delivery system using the bubblers has been developed. The PSG and BPSG film deposition processes and film properties using TEOS-Dimethylphosphite-TEB system have been studied. It is shown that the use o...
Gespeichert in:
| Datum: | 2015 |
|---|---|
| Hauptverfasser: | , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Інститут фізики напівпровідників імені В.Є. Лашкарьова НАН України
2015
|
| Schriftenreihe: | Технология и конструирование в электронной аппаратуре |
| Schlagworte: | |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/100479 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Deposition of borophosphosilicate glass films using the TEOS–dimethylphosphite–trimethylborate system / A.S. Turtsevich, O.Y. Nalivaiko // Технология и конструирование в электронной аппаратуре. — 2015. — № 1. — С. 49-58. — Бібліогр.: 34 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| Zusammenfassung: | Modernization of horizontal low pressure deposition system has been performed. The liquid source delivery system using the bubblers has been developed. The PSG and BPSG film deposition processes and film properties using TEOS-Dimethylphosphite-TEB system have been studied. It is shown that the use of dimethylphosphite allows varying the phosphorus concentration in the wide range. It is found that the optimal range of the total boron and phosphorus concentration ensuring the acceptable topology planarity and resistance to defect formation during storage is 8.7?0.3 wt% when the phosphorus concentration is 3.0—3.8 wt%. It is found that at use of the TEOS-DMP-TEB system the depletion of the phosphorus concentration along reaction zone does not occur, and the total dopant concentration is practically constant. At the same time the deposition rate of BPSG films is 9.0—10.0 nm/min and the good film thickness uniformity are ensured. The as-deposited films have “mirror-like surface” that is proof of minimal surface roughness. The BPSG films with optimal composition are characterized by the reduced reaction capability against atmospheric moisture. |
|---|