Oxidation behavior and electrochemical corrosion performance of Ti₃Al alloy with TiAl coating
Magnetron-sputter deposition was used to produce Ti–48Al–8Cr–2Ag (at.%) coating on a Ti–24Al–17Nb–0.5Mo (at.%) alloy substrate. Oxidation behavior was studied in air at 900...1000°C. The results indicated that the oxidation rate of sputtered Ti–48Al–8Cr–2Ag nanocrystalline coating was lower than tha...
Gespeichert in:
| Datum: | 2010 |
|---|---|
| Hauptverfasser: | , , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Фізико-механічний інститут ім. Г.В. Карпенка НАН України
2010
|
| Schriftenreihe: | Фізико-хімічна механіка матеріалів |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/137168 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Oxidation behavior and electrochemical corrosion performance of Ti₃Al alloy with TiAl coating / Yanjun Xi, Yongjun Liu, Zhixin Wang, Jinbin Lu // Фізико-хімічна механіка матеріалів. — 2010. — Т. 46, № 6. — С. 112-117. — Бібліогр.: 16 назв. — англ. |