Fracture Process in ± θ Laminates Subjected to Mode II Loading
This work studies the behavior of a multidirectional laminate under Mode II loading. We describe the process of delamination in a reinforced composite of glass/epoxy. The stacking sequence (plies orientation [±θ]) was selected to minimize the coupling effects. The Mode II interlaminar test under thr...
Saved in:
| Date: | 2002 |
|---|---|
| Main Authors: | , , , |
| Format: | Article |
| Language: | English |
| Published: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2002
|
| Series: | Проблемы прочности |
| Subjects: | |
| Online Access: | http://dspace.nbuv.gov.ua/handle/123456789/46873 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Journal Title: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Cite this: | Fracture Process in ± θ Laminates Subjected to Mode II Loading / A. Ahmed Benyahia, A. Laksimi, S. Benmedakhene, and X.L. Gong // Проблемы прочности. — 2002. — № 4. — С. 103-118. — Бібліогр.: 9 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of Ukraine| Summary: | This work studies the behavior of a multidirectional laminate under Mode II loading. We describe the process of delamination in a reinforced composite of glass/epoxy. The stacking sequence (plies orientation [±θ]) was selected to minimize the coupling effects. The Mode II interlaminar test under three-point bending and cantilever flexure using ENF (End Notch Flexure) and ELS (End Load Split) specimens, respectively, was performed and analyzed. The test procedures and the results of strain-energy-release rate study for crack initiation are presented. The fracture process and the mechanical behavior of the two types of specimens are analyzed. The analysis clearly shows a close link between the angle θ, the ratio a/L, and the thickness h of the specimen. Fracture by delamination can be obtained only with an optimal choice of these parameters. The analysis of the states of stresses at the tip of crack allows us to explain the phenomenon of bifurcation between plies and is confirmed by the experimental results. |
|---|