Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States
Premature fracture of steam pipelines from 14MoV6 3 steel designed for 1000,000 h service life at 540°C has been studied. Test specimens are manufactured from steel in the initial state and after 117 h of operation. Application of the local approach to fracture and the metallographic analysis,...
Gespeichert in:
| Datum: | 2004 |
|---|---|
| Hauptverfasser: | , , |
| Format: | Artikel |
| Sprache: | English |
| Veröffentlicht: |
Інститут проблем міцності ім. Г.С. Писаренко НАН України
2004
|
| Schriftenreihe: | Проблемы прочности |
| Schlagworte: | |
| Online Zugang: | http://dspace.nbuv.gov.ua/handle/123456789/47064 |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
| Zitieren: | Fracture Toughness and Crack Resistance of Steam Pipeline Steel in Initial and Used States / M. Zrilic, Z. Burzic, Z. Cvijovic // Проблемы прочности. — 2004. — № 1. — С. 68-83. — Бібліогр.: 12 назв. — англ. |