Process of intercalation of C₆₀ with molecular hydrogen from XRD data
The process of normal hydrogen infusion into a C₆₀ powder at 1 bar and room temperature was monitored using x-ray diffraction. The effect of the intercalation on the lattice proved to be rather weak: the volume expansion upon complete saturation does not exceed 0.13%. The characteristic saturation t...
Gespeichert in:
Datum: | 2009 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | English |
Veröffentlicht: |
Фізико-технічний інститут низьких температур ім. Б.І. Вєркіна НАН України
2009
|
Schriftenreihe: | Физика низких температур |
Schlagworte: | |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Назва журналу: | Digital Library of Periodicals of National Academy of Sciences of Ukraine |
Zitieren: | Process of intercalation of C₆₀ with molecular hydrogen from XRD data / K.A. Yagotintsev, Yu.E. Stetsenko, I.V. Legchenkova, A.I. Prokhvatilov, M.A. Strzhemechny, E. Schafler, M. Zehetbauer // Физика низких температур. — 2009. — Т. 35, № 3. — С. 315-319 . — Бібліогр.: 25 назв. — англ. |
Institution
Digital Library of Periodicals of National Academy of Sciences of UkraineZusammenfassung: | The process of normal hydrogen infusion into a C₆₀ powder at 1 bar and room temperature was monitored using x-ray diffraction. The effect of the intercalation on the lattice proved to be rather weak: the volume expansion upon complete saturation does not exceed 0.13%. The characteristic saturation time was found to be 320 h; the corresponding diffusion coefficient amounts to (2.8 ± 0.8)·10⁻¹⁴ cm²/s. The integrated reflection intensity calculations for completely saturated sample suggest that only octahedral voids are filled under the conditions of experiment. The effect of complete saturation on the rotational subsystem of the C₆₀ fullerite is rather weak: the orientational phase transition shifts by 6 to 7 K to lower temperatures; no essential hysteresis is noticeable. The dopant shows reluctance to leave the sample under a vacuum of 10⁻³ Torr at room temperature. |
---|